15L ISO9809 2.25M3 150bar 37MN Oxygen Tank Gas Cylinder

15 litre ISO9809 2.25M3 150bar 37MN Oxygen Tank Gas Cylinder

Information om produktet:

1、15-litre medical oxygen cylinders; 37 mn manganese steel; TUV; Medical oxygen cylinder production standard GB/T5099.3 or ISO9809-3; The outer diameter of oxygen tank is 159mm; The hydrostatic test pressure of oxygen tank is 250bar; Oxygen tank working pressure is 150bar;

2、Oxygen cylinder body height 932mm; Oxygen cylinder body weight 16.8KG; Maximum oxygen tank capacity is 2.25m3 (2250 litres); Oxygen cylinder mouth thread PZ27.8; 25E; 3/4-14 NGT, etc.; The minimum design wall thickness of oxygen cylinder is 4.3mm;

3、Alias: 15 litre gas cylinders; 2.25 m3 Oxygen tanks. 15 litre Oxygen cylinders; 15L litre Oxygen tanks; 150bar 37mn Oxygen tanks

4、Heat treatment：If the failure is considered to be due to the heat treatment applied, the manufacturer may subject all

the cylinders representing the nature of the failure to a further heat treatment, e.g. if the failure is in a

test representing the prototype or batch cylinders, test failure shall require reheat treatment of all the

represented cylinders prior to retesting.

This heat treatment shall consist of re-normalizing or re-normalizing and tempering or re-tempering.

Shandong Hongsheng Pressure Vessel Co, Ltd. er villig til at være din langsigtede partner og chef for cylindersikkerhed og i fællesskab eskortere din cylindersikkerhed.

1 、 Mindste ordremængde: Kun 100 stk.

2 、 Brug af cylindre: Vores sømløse stålcylindre bruges i vid udstrækning i industrien, medicinsk udstyr, brandbekæmpelse og videnskabelig forskning

3 、 Vi er Kinas gasflaskeproduktionsfabrik, produktsalg: Kina, Sydøstasien, Mellemøsten, Asien, Afrika, Europa, Oceanien, Amerika

4、Cylinder water pressure testing process: under the Ph of the hydraulic pressure test, the cylinder pressure holding time is not less than 30s, the pressure gauge pointer shall not fall back, and the cylinder body shall not leak or obvious deformation.  Residual deformation rate of cylinder volume is not more than 5%.

5、Tempering toughening heat treatment which follows normalizing, in which the cylinder is heated to a uniform temperature below the lower critical point, Ac1, of the steel

6、Pressure cycling test ：After the test, the cylinder bases shall be sectioned to measure the thickness and to ensure that this thickness is sufficiently close to the minimum thickness prescribed in the design and shall be within the usual production tolerances. In no case shall the actual base thickness exceed the minimum value(s) specified on the drawing by more than 15 %. The test shall be considered satisfactory if the cylinders attain the required number of cycles without developing a leak.

7、15litre Gas Cylinder Product Parameters table (ISO9809-3)