9 litre ISO9809 1.35M3 150bar 37MN Oxygen Tanks Gas Cylinder
1 、 1، الحد الأدنى لكمية الطلب: 100 فقط
2 、 استخدام الأسطوانات: تستخدم أسطواناتنا الفولاذية غير الملحومة على نطاق واسع في الصناعة والأجهزة الطبية ومكافحة الحرائق والبحث العلمي
3 、 نحن مصنع إنتاج أسطوانات الغاز في الصين، مبيعات المنتجات: الصين، جنوب شرق آسيا، الشرق الأوسط، الشرق الأوسط، آسيا، أفريقيا، أوروبا، أوقيانوسيا، أمريكا
4、Cylinder mouth thread processing process: after the thread is processed, it is measured by light gauge and plug gauge. The lower end of the chamfering of the bottle mouth and the base surface of the plug gauge are up to the standard. (Commonly used thread: PZ19.2; PZ27.8; PZ39; 25E; 3/4-14 NGT, etc.). The effective number of thread threads 7~8 buckle, general processing thread buckle number between 10~15 buckle.
5、This part of ISO 9809 addresses the general requirements on design, construction and initial inspection and testing of pressure receptacles of the United Nations Recommendations on the Transport of Dangerous Goods: Model Regulations.
6、9 litre Gas Cylinder Product
Parameters table (ISO9809-3)
| النوع | في الخارج
القطر (مم) |
المياه
القدرة الاستيعابية (L) |
زجاجة
الارتفاع (مم) |
الوزن
（كغ) |
العمل
الضغط （البار） |
تصميم الحائط
السُمك （م) |
المواد
الدرجات |
| WMAⅡ140-9.0L-150 | 140 | 9.0 | 744 | 10.7 | 150 | 3.8 | 37MN |
| WMⅡ159-9.0L-150 | 159 | 9.0 | 600 | 10.5 | 150 | 3.9 | 37MN |
معلومات المنتج:
1、9 litre oxygen cylinders; 37 mn manganese steel; Gas cylinder production standard GB/T5099.3 or ISO9809-3; The outer diameter of the cylinder is 140mm; Oxygen cylinder hydrostatic test pressure is 250bar; Working pressure is 150bar;
2、Oxygen cylinder body height 744mm; Oxygen cylinder weight 10.7kg; Oxygen cylinder mouth thread PZ19.2,PZ27.8,PZ39; 25E; 3/4-14 NGT, etc.; Maximum oxygen tank capacity is 1.35m3 (1350 litres); The minimum design wall thickness of oxygen cylinder is 3.8mm;
3、Aliases: 9 litre gas cylinders; 1.35 m3 Oxygen tanks. 9 litre Oxygen cylinders; 9 litre Oxygen tanks; 9 litre 150bar Oxygen gas tank.
4、Calculation of convex ends (heads and bases)
7.3.1 The thickness, at the centre of a convex end shall be not less than that required by the following
criteria: where the inside knuckle radius, r, is not less than 0,075 D, then:
To obtain a satisfactory stress distribution in the region where the end joins the shell, any thickening of the
end that may be required shall be gradual from the point of juncture, particularly at the base.
For the application of this rule, the point of juncture between the shell and the end is defined by the horizontal lines indicating dimension
الشكل (ب) لا يُستثنى من هذا الشرط.
إن شركة Shandong Hongsheng لأوعية الضغط المحدودة على استعداد لأن تكون شريكك على المدى الطويل وكبير مسؤولي سلامة الأسطوانات، وأن ترافق سلامة الأسطوانة الخاصة بك بشكل مشترك.